Structures by: Mareschal J.
Total: 17
Praseodymium(II) chromate
CrO4Pr
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.344Å b=7.344Å c=6.428Å
α=90° β=90° γ=90°
Neodymium(II) chromate
CrNdO4
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.311Å b=7.311Å c=6.402Å
α=90° β=90° γ=90°
Europium(II) chromate
CrEuO4
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.223Å b=7.223Å c=6.33Å
α=90° β=90° γ=90°
Gadolinium(II) chromate
CrGdO4
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.204Å b=7.204Å c=6.315Å
α=90° β=90° γ=90°
Dysprosium(II) chromate
CrDyO4
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.143Å b=7.143Å c=6.274Å
α=90° β=90° γ=90°
Terbium(II) chromate
CrO4Tb
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.17Å b=7.17Å c=6.294Å
α=90° β=90° γ=90°
Holmium(II) chromate
CrHoO4
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.12Å b=7.12Å c=6.255Å
α=90° β=90° γ=90°
Erbium(II) chromate
CrErO4
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.093Å b=7.093Å c=6.23Å
α=90° β=90° γ=90°
Ytterbium(II) chromate
CrO4Yb
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.058Å b=7.058Å c=6.216Å
α=90° β=90° γ=90°
Yttrium(II) chromate
CrO4Y
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.112Å b=7.112Å c=6.251Å
α=90° β=90° γ=90°
Lutetium(II) chromate
CrLuO4
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.027Å b=7.027Å c=6.2Å
α=90° β=90° γ=90°
Dysprosium chromium oxide
CrDyO3
Journal de Physique (Paris) (1968) 29, 67-73
a=5.263Å b=5.52Å c=7.552Å
α=90° β=90° γ=90°
Erbium chromium oxide
CrErO3
Solid State Communications (1967) 5, 93-97
a=5.223Å b=5.516Å c=7.519Å
α=90° β=90° γ=90°
Neodymium chromium oxide
CrNdO3
Solid State Communications (1967) 5, 93-97
a=5.425Å b=5.478Å c=7.694Å
α=90° β=90° γ=90°
Samarium(II) chromate
CrO4Sm
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1964) 259, 411-413
a=7.251Å b=7.251Å c=6.356Å
α=90° β=90° γ=90°
Yttrium aluminium oxide
AlO3Y
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences (1884 - 1965) (1963) 257, 867-870
a=3.680(5)Å b=3.680(5)Å c=10.52(1)Å
α=90° β=90° γ=120°
Terbium iron(III) oxide
FeO3Tb
Solid State Communications (1967) 5, 293-298
a=5.326Å b=5.602Å c=7.635Å
α=90° β=90° γ=90°